- Hydrotalcite
- Highly transparent hydrotalcite
- Catalyst carrier hydrotalcite
- Flame retardant hydrotalcite
- Stabilizer hydrotalcite
- Agricultural film hydrotalcite
- Nucleating agent hydrotalcite
- Magnesium hydroxide
- Mineral-derived magnesium hydroxide D100
- Synthesized magnesium hydroxide D110
- Electronic grade magnesium hydroxide D120
- Chemical method magnesium hydroxide D5
- Chemical method magnesium hydroxide D6
- Flame retardant
- Rubber specific flame retardant D130
- Efficient flame retardant D320/D320MD
- Efficient flame retardant D320T
- Efficient flame retardant H5VA/D330
- Thermal insulation materials
- Automotive lining
- Automotive insulation materials
- New energy battery insulation film
- Industrial insulation materials
Thermal insulation materials
Product Introduction
The A&H-CFP series products are made by vacuum forming special ceramic fibers and adding special binders in a composite; Maintain good mechanical strength, resistance to airflow impact, and hydrophobicity after heating.
Excellent thermal and chemical stability.
·Non flammable, low thermal conductivity, low heat fusion.
·Product flatness.
·Good thermal insulation performance.
·High sound insulation and mechanical strength.
·Superior mechanical and structural strength.
The A&H-CFP series products are made by vacuum forming special ceramic fibers and adding special binders in a composite; Maintain good mechanical strength, resistance to airflow impact, and hydrophobicity after heating.
Excellent thermal and chemical stability.
·Non flammable, low thermal conductivity, low heat fusion.
·Product flatness.
·Good thermal insulation performance.
·High sound insulation and mechanical strength.
·Superior mechanical and structural strength.
Product Application
·Ceramic/glass/metallurgical kiln hot surface backing.
·Muffle furnace backing.
·Building protection and sound insulation.
·Ceramic/glass/metallurgical kiln hot surface backing.
·Muffle furnace backing.
·Building protection and sound insulation.
Physical property
|
Item |
A&H-CFP1700 |
A&H-CFP1800 |
|
Classification Temperature, ℃ |
1700 |
1800 |
|
Density (kg/m³) |
400 |
400 |
|
Linear Shrinkage ℃*24h |
1 (1600) |
0.8 (1600) |
|
Flexural Strength (MPa@25℃) |
0.72 |
0.72 |
|
Expansion Rate@600℃ |
≤0.28 |
≤0.28 |
|
Thermal Conductivity (W/m·k) |
0.147@400℃ |
/ |
|
0.186@600℃ |
0.211@800℃ |
|
|
0.236@800℃ |
0.232@1200℃ |
|
|
0.296@1000℃ |
0.301@1400℃ |
|
|
Chemical Composition |
Al₂O₃(%)75-88 SiO₂(%)12-25 |
Al₂O₃(%)78-90 SiO₂(%)10-22 |
|
Item |
A&H-CFP1700 |
A&H-CFP1800 |
|
Classification Temperature, ℃ |
1700 |
1800 |
|
Density (kg/m³) |
400 |
400 |
|
Linear Shrinkage ℃*24h |
1 (1600) |
0.8 (1600) |
|
Flexural Strength (MPa@25℃) |
0.72 |
0.72 |
|
Expansion Rate@600℃ |
≤0.28 |
≤0.28 |
|
Thermal Conductivity (W/m·k) |
0.147@400℃ |
/ |
|
0.186@600℃ |
0.211@800℃ |
|
|
0.236@800℃ |
0.232@1200℃ |
|
|
0.296@1000℃ |
0.301@1400℃ |
|
|
Chemical Composition |
Al₂O₃(%)75-88 SiO₂(%)12-25 |
Al₂O₃(%)78-90 SiO₂(%)10-22 |
Product standard specifications
|
Classification Temperature, ℃ |
Bulk Density, kg/m³ |
Length, mm |
Width, mm |
Thickness, mm |
|
1700 |
400/450 |
1000/900 |
600 |
25/30/40/50 |
|
1800 |
400/450 |
1000/900 |
600 |
25/30/40/50 |
|
Classification Temperature, ℃ |
Bulk Density, kg/m³ |
Length, mm |
Width, mm |
Thickness, mm |
|
1700 |
400/450 |
1000/900 |
600 |
25/30/40/50 |
|
1800 |
400/450 |
1000/900 |
600 |
25/30/40/50 |